CORE DYNEEMA SK78 XTR ... .....
The excellent creep qualities combined with a tenacity of 39,8 gr/denx and a modulus of 1.314 gr/den allow the construction of an extremely resistant and reactive rope, dedicated to maneuvers subjected to high static and dynamic loads.
Thanks to the reduced specific weight of 0.974 kg/dm3 the rope is extremely light, while the protective treatment with a mix of polyurethane resins makes it water-repellent and highly resistant to wear.
The hot pre-stretch treatment called XTR takes the diameter/load ratio to the extreme by reducing the section and at the same time increasing the breaking load.
COVER HI-TECH COVER COLLECTION
La nostra treccia tecnica SK78 XTR puo' essere fornita sia scalzata che calzata spaziando in una vasta e completa gamma di soluzioni appositamente studiate per il racing .
Nella tabella seguente vengono esposte le caratteristiche tecniche della cima DYNEEMA SK78 XTR-PU scalzata
| anima copertura |
DYNEEMA SK78 XTR-PU assente |
|
| Sezione | Carico di rottura |
peso |
| mm | daN | gr/mt |
| 1 | 210 | 1,2 |
| 1,5 | 330 | 1,8 |
| 2 | 450 | 2,5 |
| 2,5 | 750 | 3,6 |
| 3 | 1.050 | 4,8 |
| 3,5 | 1.350 | 8,0 |
| 4 | 2.300 | 9,9 |
| 5 | 3.000 | 15,0 |
| 6 | 4.700 | 23,5 |
| 7 | 6.510 | 30,5 |
| 8 | 8.250 | 37,5 |
| 9 | 9.430 | 50,0 |
| 10 | 12.080 | 58,8 |
| 11 | - | - |
| 12 | 16.000 | 92,1 |
| 13 | - | - |
| 14 | 20.900 | 125,5 |
| 15 | - | - |
| 16 | 25.500 | 156,8 |
| 18 | - | - |
| 20 | - | - |
II valori medi indicati sono ricavati dai test del laboratorio Benvenuti su cime nuove e possono essere variati senza preavviso. Sono disponibili altri diametri su richiesta. Il carico statico della cima non deve superare il 20% dei carichi di rottura indicati in tabella. Il nodo pregiudica il carico di rottura con riduzioni fino al 60%. L'impiombatura aumenta il diametro di circa 1,5 volte. L'esposizione agli agenti atmosferici determina riduzioni dei carichi di rottura delle cime, a seconda dell'intensità e durata della stessa e anche in base alla composizione e costruzione del prodotto.
Alla sezione Hi-Tech Cover Collection e possibile scegliere tra 6 calze tecniche suddivise in 2 gruppi
I° GRUPPO ) Calze resistenti a strappi , forti abrasioni e picchi di temperatura
II° GRUPPO ) Calze ad alto grip e forte resistenza agli strappi
High Tech Cover Collection
-
BTEC-DYN Cover
EXCELLENT RES. strain, abrasion and temperature1 COLORI_DISPONIBILI: NOT FOUND -
-
BTEC-DYN-PET Cover
EXCELLENT RES. strain, abrasion and temperature5 COLORI_DISPONIBILI: NOT FOUND -
-
BTEC-PET Cover
EXCELLENT RES. strain, abrasion and temperature5 COLORI_DISPONIBILI: NOT FOUND -
-
CRD-DYN-PET Cover
ELEVATED RES. strain , abrasions and temperatures5 COLORI_DISPONIBILI: NOT FOUND -
CRD-PET Cover
ELEVATED RES. strain , abrasions and temperatures5 COLORI_DISPONIBILI: NOT FOUND -
PET Cover
ELEVATED RES. strain , abrasions and temperatures6 COLORI_DISPONIBILI: NOT FOUND
The following table shows the technical characteristics of the DYNEEMA SK78 XTR-PU line , both uncovered and with a technical cover .
| DYNEEMA SK78 XTR-PU |
DYNEEMA SK78 XTR-PU + CALZE TECNICHE |
|||||||||
| Ø | SK78 XTR-PU TRECCIA SCALZATA |
Ø | SK78 XTR-PU + CALZE TECNICHE |
B.technora Dyneema |
B.Technora Dyneema Poliestere |
B.Technora Poliestere | Cordura Dyneema Poliestere | Cordura Poliestere | Poliestere | |
| Section | Breaking load |
peso | Sezione | Breaking load |
peso | peso | peso | peso | peso | peso |
| mm | daN | gr/mt | mm | daN | gr/mt | gr/mt | gr/mt | gr/mt | gr/mt | gr/mt |
| 1 | 210 | 1,2 | 1 | - | - | - | - | - | - | - |
| 1,5 | 330 | 1,8 | 1,5 | - | - | - | - | - | - | - |
| 2 | 450 | 2,5 | 2 | 210 | 4,6 | 4,6 | 4,6 | 4,1 | 4,6 | 4,6 |
| 2,5 | 750 | 3,6 | 2,5 | 330 | 5,7 | 5,6 | 5,6 | 5,0 | 5,5 | 5,4 |
| 3 | 1.050 | 4,8 | 3 | 450 | 7,4 | 7,4 | 7,5 | 6,6 | 7,3 | 7,2 |
| 3,5 | 1.350 | 8,0 | 3,5 | 750 | 9,1 | 9,1 | 9,2 | 8,1 | 8,9 | 8,8 |
| 4 | 2.300 | 9,9 | 4 | 1.050 | 12,3 | 12,1 | 12,4 | 10,9 | 13,0 | 12,9 |
| 5 | 3.000 | 15,0 | 5 | 1.350 | 18,8 | 18,6 | 19,0 | 16,7 | 18,5 | 18,3 |
| 6 | 4.700 | 23,5 | 6 | 2.300 | 25,9 | 25,6 | 26,2 | 23,0 | 25,2 | 24,9 |
| 7 | 6.510 | 30,5 | 7 | 3.000 | 38,0 | 37,5 | 38,1 | 33,7 | 36,9 | 36,5 |
| 8 | 8.250 | 37,5 | 8 | 3.900 | 49,7 | 49,0 | 50,0 | 44,2 | 48,3 | 47,8 |
| 9 | 9.430 | 50,0 | 9 | 4.700 | 60,0 | 59,2 | 60,7 | 53,2 | 58,2 | 57,6 |
| 10 | 12.080 | 58,8 | 10 | 6.510 | 71,0 | 69,9 | 71,3 | 63,0 | 68,8 | 68,1 |
| 11 | - | - | - | - | - | - | - | - | - | - |
| 12 | 16.000 | 92,1 | 12 | 9.430 | 101,0 | 99,5 | 101,5 | 89,5 | 98,0 | 97,0 |
| 13 | - | - | - | - | - | - | - | - | - | - |
| 14 | 20.900 | 125,5 | 14 | 12.080 | 136,0 | 133,7 | 136,5 | 120,4 | 131,7 | 130,4 |
| 15 | - | - | - | - | - | - | - | - | - | - |
| 16 | 25.500 | 156,8 | 16 | 16.000 | 180,0 | 177,4 | 181,0 | 159,6 | 174,7 | 173,0 |
| 18 | - | - | 18 | 20.900 | 212,2 | 208,8 | 213,1 | 188,0 | 205,0 | 203,0 |
| 20 | - | - | 20 | 22.000 | 265,0 | 261,1 | 266,5 | 235,0 | 257,0 | 254,4 |
The average values indicated are obtained from tests in the Benvenuti company laboratory on new line and may be changed without any notice. Other diameters are available on request. The static load of the rope must not exceed 20% of the breaking loads indicated in the table. The knot affects the breaking load with reductions of up to 60%. Splicing increases the diameter approximately 1.5 times. Exposure to atmospheric agents determines reductions in the breaking loads of the ropes, depending on the intensity and duration of the same and also on the composition and construction of the product.