CARATTERISTICHE_TECNICHE: NOT FOUND
CORE COVER
Peak resistance temp 650 °C 353 °C
Tenacity 37.0 cN/dTex 26.5 cN / dTex
Coeff. of friction 0,18 0,12
Grip winch / stopper excellent great
Smoothness moderate good
Abrasion res. excellent excellent
Specific weight 1,56 kg/dm 1,30 kg/dm3
Res. to continuous work excellent excellent
UTILIZZO: NOT FOUND
Maneuvers with extreme ratio
Frictions / Load / Temperature
- PBO inserts to maximize resistance to tearing, heat and abrasion
- Dyneema inserts to make the rope smoother
- Polyester inserts to differentiate the colors
Frictions / Load / Temperature
- PBO inserts to maximize resistance to tearing, heat and abrasion
- Dyneema inserts to make the rope smoother
- Polyester inserts to differentiate the colors
RICHIEDI_INFO: NOT FOUND
GAMMA_COLORI: NOT FOUND:
CORE DYNEEMA SK99 XTR
The creep is totally absent of this fiber; this, combined with a tenacity of 37 cn/dTex and a module of 1720 cN/dTex, make it possible to build an extremely resistant but above all extremely reactive line, dedicated to maneuvers subjected to high static and dynamic loads.
The specific weight of 1,56 kg/dm3 means that the rope is heavier than a Dyneema rope, however the melting point of 650 °C allows unthinkable applications for the latter; the protective treatment with a mix of polyurethane resins makes it water-repellent and highly resistant to wear.
The hot per-stretch treatment called XTR takes the diameter / load ratio to the extreme by reducing the section and increasing the breaking load at the same time.
COVER PBO ZYLON / DYNEEMA / POLIESTERE
It is a highly technical cover dedicated to extreme loads, temperatures and frictions.
The PBO Zylon inserts greatly increase the resistance to abrasion and to the high temperatures generated by very strong friction during the change of maneuvers.
The tolerance point at high temperatures is extreme, guaranteeing a resistance to peaks of 353 °C.
The friction coefficient of 0.12 makes it very gripping both in the hand and on winch and stoppers.
The Dyneema inserts reinforce the cover bringing its toughness to 26.5 cN / dTex ensuring extreme efficiency on winches and chokes.
The range of colors is wide thanks to the polyester components that make the maneuvers easily recognizable.
The creep is totally absent of this fiber; this, combined with a tenacity of 37 cn/dTex and a module of 1720 cN/dTex, make it possible to build an extremely resistant but above all extremely reactive line, dedicated to maneuvers subjected to high static and dynamic loads.
The specific weight of 1,56 kg/dm3 means that the rope is heavier than a Dyneema rope, however the melting point of 650 °C allows unthinkable applications for the latter; the protective treatment with a mix of polyurethane resins makes it water-repellent and highly resistant to wear.
The hot per-stretch treatment called XTR takes the diameter / load ratio to the extreme by reducing the section and increasing the breaking load at the same time.
COVER PBO ZYLON / DYNEEMA / POLIESTERE
It is a highly technical cover dedicated to extreme loads, temperatures and frictions.
The PBO Zylon inserts greatly increase the resistance to abrasion and to the high temperatures generated by very strong friction during the change of maneuvers.
The tolerance point at high temperatures is extreme, guaranteeing a resistance to peaks of 353 °C.
The friction coefficient of 0.12 makes it very gripping both in the hand and on winch and stoppers.
The Dyneema inserts reinforce the cover bringing its toughness to 26.5 cN / dTex ensuring extreme efficiency on winches and chokes.
The range of colors is wide thanks to the polyester components that make the maneuvers easily recognizable.
| Diameter | mm | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 16 | 18 | 20 |
| Breacking load | daN | 2.200 | 3.500 | 4.750 | 5.750 | 6.600 | 8.640 | 10.500 | 11.550 | 12.830 | 14.100 | 17.300 | 21.100 |
| Weight | gr/mt | 30,0 | 45,0 | 58,4 | 72,6 | 81,2 | 104,0 | 119,3 | 138,1 | 158,4 | 206,9 | 261,4 | 326,7 |
The average values indicated are obtained from the laboratory tests Welcome to new buds and can be changed without notice. Other diameters are available on request. The static load of the rope must not exceed 20% of the breaking loads indicated in the table. The knot affects the breaking load with reductions of up to 60%. The splice increases the diameter by approximately 1.5 times. Exposure to atmospheric agents determines reductions in the breaking loads of the buds, depending on the intensity and duration of the same and also on the composition and construction of the product.